| Customization: | Available |
|---|---|
| Application: | Aerospace, Architectural, Ceramic Decorations, Electronics, Home Use, Medical, Refractory |
| Flexural Strength: | >1000 MPa |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| PSZ Ceramic Properties | ||
| PROPERTIES | Unit | Zirconia Ceramic |
| Al2O3 (ZrO2 )Content | wt% | ≥ 94 |
| Density | G /CM3 | 6.00 |
| Hardness (HRA) | HRA ≥ | 90 |
| Flexural Strength | MPa ≥ | 800 |
| Max. use Temperature | ºC | 1000 |
| Gas-tightness | Pass | |
| Thermal shock Resistance | Pass | |
| Coeff. of Thermal exp. | ×10-6/ºC | 10.0 |
| Volume Resistivity | Ω·cm 20ºC | 1014 |
| Dielectric Strength | KV/mm , DC≥ | 20 |
| Acid Resistance | mg/cm2 ≤ | 2.0 |
| Alkali Resistance | mg/cm2 ≤ | 0.08 |
| Wear ability | g/cm2 ≤ | 0.05 |
| Compressive Strength | M Pa ≥ | 2000 |
| Tensile Strength | M Pa ≥ | 600 |
| Elastic Modulus(Young) | G Pa | 320 |
| Thermal Conductivity | W/m·K( 20ºC) | 2.6 |
| Y-FSZ Ceramic Properties | ||
| Chemical content | ZrO2 | 86 wt% |
| Y2O3 | 14 wt% | |
| Physical Properties |
Melting point | ≥2500ºC |
| Max. operating temperature | 2200ºC | |
| Color | White | |
| Density | 5.8g/cm3 | |
| Mechanical properties | Flexural strength | 200MPa |
| Young's module | 200GPa | |
| Hardness(HRA) | 86 | |
| Thermal properties | Thermal expansion coefficient(20ºC) | 8-10X10-6 |
| Thermal conductivity | 1-2W/mk | |
| Electrical properties | Dielectric constant(1MHz25ºC) | 12 |
| Electrical resistivity(25ºC) | 109 | |